1. Commonly used media for seamless steel pipe pickling:

Sulfuric acid, nitric acid, phosphoric acid, hydrofluoric acid. When pickling, be sure to add pickling corrosion inhibitor to prevent the acid from corroding the metal.

2. Seamless steel pipe pickling process

There are mainly immersion pickling method, spray pickling method and acid paste derusting method. Generally, the dipping and pickling method is used, and the spray method can be used in mass production. Steel parts are generally pickled in a 10%-20% (volume) sulfuric acid solution at a temperature of 40°C. When the iron content in the solution exceeds 80g/L and the ferrous sulfate exceeds 215g/L, the pickling solution should be replaced. At room temperature, the steel is pickled with 20% to 80% (volume) hydrochloric acid solution to prevent over-corrosion and hydrogen embrittlement. Since acid has a great corrosive effect on metals, corrosion inhibitors need to be added. After cleaning, the metal surface becomes silvery white, and the surface is passivated to improve the corrosion resistance of stainless steel. In order to eliminate the surface adsorption of the diatomaceous earth carrier and reduce the tailing of the chromatographic peak, the carrier needs to be acid washed or alkaline washed before use. Pickling is to soak the carrier with 6mol/L hydrochloric acid for 2 hours or heat and soak with concentrated hydrochloric acid for 30 minutes, filter, wash with water to neutrality, and dry. Pickling can remove iron, aluminum, calcium, magnesium and other impurities on the surface, but cannot remove silanol groups. The pickling carrier is suitable for the analysis of acidic samples.

3. Seamless steel pipe pickling effect

Degreasing and derusting the surface of precision seamless steel pipes(astm a53 pipes) to prepare for the next process. In the production process, the pickling process is to remove the surface oxide scale, and then go through lubrication treatment (carbon steel-phosphorous saponification, stainless steel-butter lime, copper aluminum pipe-oiling), using the old process-copper plating), and then For drawing and deep processing. If the steel pipe is not pickled, there may be oxides and oil stains on the surface, and the nuclear energy of the phosphating solution cannot remove them, and the quality of phosphating will be reduced.